Does Treating Metal Reduce The Effects Of

Weathering In A California Climate? Essay, Research Paper

Does handling metal cut down the effects of enduring in a California clime? This experiment trades with the elements of conditions against metal ; air current, rain, solar radiation, oxidization ( unifying a substance with O ) , and heat ( the presence and absence of ) . My hypothesis is that the painted protected metal will do better than the au naturel metal during the weathering. The ground I believe this will go on is that the protected metal has that excess bed, so it will be harder for the barrage of alterations to ache the metal.

The protectants for metals include assorted types of touch-up pigments, glosss and waxes, organic structure fillers, washes, and assorted other types of chemicals. Metal protection is most present in the automotive visual aspect industry. Of the three major sections of the market, colour waxes lead with 36 % of gross revenues ; protectants follow with 27 % , and touch-up pigments account for merely over 26 % . Chain retail merchants carry an norm of 1.5 lines of touch-up pigments and 5.5 lines of waxes/polishes. The mean figure of protectants in aftermarket mercantile establishments is three. Harmonizing to a market research study, 69.9 million people, or 37 % of American grownups, usage auto wax or Polish. ( hypertext transfer protocol: //www.findsvp.com/tocs/ML0165.htm )

The reaction of O with a metal consequences in the formation of a metal oxide graduated table which in most instances protects the implicit in metal against farther corrosion. Contamination of the air, e.g. with C dioxide, S dioxide and H2O, accelerates the oxidization rate well. The temperature at which the oxidization graduated table is formed depends on the chemical composing of the metal metal.

Alseal 518 is a surfacing composing formulated for protecting ferric metals from both high temperature heat oxidization and at the same clip offer sacrificial ( cathodic ) protection to the base metal. Because of its high temperature capablenesss, it offers protection when exposed to cyclic high temperature and caustic salt environments ( like a California clime ) ; it provides thermic stableness. Trials have been conducted utilizing low C steel metals. There was no loss of weight after several hebdomads uninterrupted exposure at 1000.F. After exposure to 5 % salt spray for 1000 hours, there was no grounds of corrosion. The coated metal will non check, spall, or fail after flooring from 1100.F to room temperature repeatedly. ( hypertext transfer protocol: //www1.che.ufl.edu/meeting/1997/annual/session/81/a/index.html )

For an oxide to be protective the oxide-metal volume ratio must be slightly larger than the integrity, the oxide must maintain good unity and must stay adherent to the substrate. Chromium every bit good as Ni, Si, and aluminium are used as debasing elements to better the oxidization opposition in metals. ( hypertext transfer protocol: //www.metalogic.be/MatWeb/reading/gas/ka_ht/hto2mat.htm )

Materials

a long piece of metal ; a auto door ( 4 x4 )

a can of wax

a smoother

Procedure

1. The metal will be divided into three subdivisions.

2. The 1st subdivision will be stripped down to the bare metal.

3. The 2nd subdivision will merely hold pigment.

4. The 3rd subdivision will be covered in one bed of wax.

5. The metal will be exposed to the conditions.

6. I will sporadically analyze it for harm or eroding.