Powder Metallurgy

10 October 2016

Powder metallurgy is the process of blending fine powdered materials, pressing them into a desired shape or form (compacting), and then heating the compressed material in a controlled atmosphere to bond the material (sintering). The powder metallurgy process generally consists of four basic steps: (1) powder manufacture, (2) powder blending,(3) compacting, (4) sintering. Compacting is generally performed at room temperature, and the elevated-temperature process of sintering is usually conducted at atmospheric pressure. Optional secondary processing often follows to obtain special properties or enhanced precision. 1] Two main techniques used to form and consolidate the powder are sintering and metal injection molding. Recent developments have made it possible to use rapid manufacturing techniques which use the metal powder for the products. Because with this technique the powder is melted and not sintered, better mechanical strength can be accomplished. History and capabilities The history of powder metallurgy (PM) and the art of metals and ceramics sintering are intimately related to each other. Sintering involves the production of a hard solid metal or ceramic piece from a starting powder. While a crude form of iron powder metallurgy existed in Egypt as early as 3000 B. C, and the ancient Incas made jewelry and other artifacts from precious metal powders, mass manufacturing of P/M products did not begin until the mid-or late- 19th century”. [2] In these early manufacturing operations, iron was extracted by hand from metal sponge following reduction and was then reintroduced as a powder for final melting or sintering. A much wider range of products can be obtained from powder processes than from direct alloying of fused materials.

We will write a custom essay sample on
Powder Metallurgy
or any similar topic specifically for you
Do Not Waste
Your Time
HIRE WRITER

In melting operations the “phase rule” applies to all pure and combined elements and strictly dictates the distribution of liquid and solid phases which can exist for specific compositions. In addition, whole body melting of starting materials is required for alloying, thus imposing unwelcome chemical, thermal, and containment constraints on manufacturing. Unfortunately, the handling of aluminium/iron powders poses major problems. [3] Other substances that are especially reactive with atmospheric oxygen, such as tin, are sinterable in special atmospheres or with temporary coatings. 4] In powder metallurgy or ceramics it is possible to fabricate components which otherwise would decompose or disintegrate. All considerations of solid-liquid phase changes can be ignored, so powder processes are more flexible than casting, extrusion, or forging techniques. Controllable characteristics of products prepared using various powder technologies include mechanical, magnetic,[5] and other unconventional properties of such materials as porous solids, aggregates, and intermetallic compounds. Competitive characteristics of manufacturing processing (e. g. , tool wear, complexity, or vendor options) also may be closely regulated.

Powder Metallurgy products are today used in a wide range of industries, from automotive and aerospace applications to power tools and household appliances. Each year the international PM awards highlight the developing capabilities of the technology. [6] Isostatic powder compacting Isostatic powder compacting is a mass-conserving shaping process. Fine metal particles are placed into a flexible mould and then high gas or fluid pressure is applied to the mould. The resulting article is then sintered in a furnace. This increases the strength of the part by bonding the metal particles.

This manufacturing process produces very little scrap metal and can be used to make many different shapes. The tolerances that this process can achieve are very precise, ranging from +/- 0. 008 inches (0. 2 mm) for axial dimensions and +/- 0. 020 inches (0. 5 mm) for radial dimensions. This is the most efficient type of powder compacting. (The following subcategories are also from this reference. )[7] This operation is generally applicable on small production quantities, as it is more costly to run due to its slow operating speed and the need for expendable tooling. oda[8] Compacting pressures range from 15,000 psi (100,000 kPa) to 40,000 psi (280,000 kPa) for most metals and approximately 2,000 psi (14,000 kPa) to 10,000 psi (69,000 kPa) for non-metals. The density of isostatic compacted parts is 5% to 10% higher than with other powder metallurgy processes. Equipment There are many types of equipment used in Powder Compacting. There is the mold, which is flexible, a pressure mold that the mold is in, and the machine delivering the pressure. There are also controlling devices to control the amount of pressure and how long the pressure is held for.

The machines need to apply anywhere from 15,000 psi to 40,000 psi for metals. Geometrical Possibilities Typical workpiece sizes range from 0. 25 in (6. 35 mm) to 0. 75 in (19. 05 mm) thick and 0. 5 in (12. 70 mm) to 10 in (254 mm) long. It is possible to compact workpieces that are between 0. 0625 in (1. 59 mm) and 5 in (127 mm) thick and 0. 0625 in (1. 59 mm) to 40 in (1,016 mm) long. Tool style Isostatic tools are available in three styles, free mold (wet-bag), coarse mold(damp-bag), and fixed mold (dry-bag). The free mold style is the traditional style of isostatic compaction and is not generally used for high production work.

In free mold tooling the mold is removed and filled outside the canister. Damp bag is where the mold is located in the canister, yet filled outside. In fixed mold tooling, the mold is contained within the canister, which facilitates automation of the process. Hot isostatic pressing Hot isostatic pressing (HIP) compresses and sinters the part simultaneously by applying heat ranging from 900°F (480°C) to 2250°F (1230°C). Argon gas is the most common gas used in HIP because it is an inert gas, thus prevents chemical reactions during the operation. Cold isostatic pressing

Cold isostatic pressing (CIP) uses fluid as a means of applying pressure to the mold at room temperature. After removal the part still needs to be sintered. Design Considerations Advantages over standard powder compaction are the possibility of thinner walls and larger workpieces. Height to diameter ratio has no limitation. No specific limitations exist in wall thickness variations, undercuts, reliefs, threads, and cross holes. No lubricants are need for isostatic powder compaction. The minimum wall thickness is 0. 05 inches (1. 27 mm) and the product can have a weight between 40 and 300 pounds (18 and 136 kg).

There is 25 to 45% shrinkage of the powder after compacting. Powder production techniques Any fusible material can be atomized. Several techniques have been developed which permit large production rates of powdered particles, often with considerable control over the size ranges of the final grain population. Powders may be prepared by comminution, grinding, chemical reactions, or electrolytic deposition. Powders of the elements titanium, vanadium, thorium, niobium, tantalum, calcium, and uranium have been produced by high-temperature reduction of the corresponding nitrides and carbides.

Iron, nickel, uranium, and beryllium submicrometre powders are obtained by reducing metallic oxalates and formates. Exceedingly fine particles also have been prepared by directing a stream of molten metal through a high-temperature plasma jet or flame, simultaneously atomizing and comminuting the material. On Earth various chemical- and flame-associated powdering processes are adopted in part to prevent serious degradation of particle surfaces by atmospheric oxygen. Atomization Atomization is accomplished by forcing a molten metal stream through an orifice at moderate pressures.

A gas is introduced into the metal stream just before it leaves the nozzle, serving to create turbulence as the entrained gas expands (due to heating) and exits into a large collection volume exterior to the orifice. The collection volume is filled with gas to promote further turbulence of the molten metal jet. On Earth, air and powder streams are segregated using gravity or cyclonic separation. Most atomised powders are annealed, which helps reduce the oxide and carbon content. The water atomized particles are smaller, cleaner, and nonporous and have a greater breadth of size, which allows better compacting.

Simple atomization techniques are available in which liquid metal is forced through an orifice at a sufficiently high velocity to ensure turbulent flow. The usual performance index used is the Reynolds number R = fvd/n, where f = fluid density, v = velocity of the exit stream, d = diameter of the opening, and n = absolute viscosity. At low R the liquid jet oscillates, but at higher velocities the stream becomes turbulent and breaks into droplets. Pumping energy is applied to droplet formation with very low efficiency (on the order of 1%) and control over the size distribution of the metal particles produced is rather poor.

Other techniques such as nozzle vibration, nozzle asymmetry, multiple impinging streams, or molten-metal injection into ambient gas are all available to increase atomization efficiency, produce finer grains, and to narrow the particle size distribution. Unfortunately, it is difficult to eject metals through orifices smaller than a few millimeters in diameter, which in practice limits the minimum size of powder grains to approximately 10 ? m. Atomization also produces a wide spectrum of particle sizes, necessitating downstream classification by screening and remelting a significant fraction of the grain boundary.

Centrifugal disintegration Centrifugal disintegration of molten particles offers one way around these problems. Extensive experience is available with iron, steel, and aluminium. Metal to be powdered is formed into a rod which is introduced into a chamber through a rapidly rotating spindle. Opposite the spindle tip is an electrode from which an arc is established which heats the metal rod. As the tip material fuses, the rapid rod rotation throws off tiny melt droplets which solidify before hitting the chamber walls.

A circulating gas sweeps particles from the chamber. Similar techniques could be employed in space or on the Moon. The chamber wall could be rotated to force new powders into remote collection vessels,[9] and the electrode could be replaced by a solar mirror focused at the end of the rod. An alternative approach capable of producing a very narrow distribution of grain sizes but with low throughput consists of a rapidly spinning bowl heated to well above the melting point of the material to be powdered.

Liquid metal, introduced onto the surface of the basin near the center at flow rates adjusted to permit a thin metal film to skim evenly up the walls and over the edge, breaks into droplets, each approximately the thickness of the film. [10] Other techniques Another powder-production technique involves a thin jet of liquid metal intersected by high-speed streams of atomized water which break the jet into drops and cool the powder before it reaches the bottom of the bin. In subsequent operations the powder is dried. This is called water atomisation.

The advantage is that metal solidifies faster than by gas atomization since the heat capacity of water is some magnitudes higher, mainly a result of higher density. Since the solidification rate is inversely proportional to the particle size smaller particles can be made using water atomisation. The smaller the particles, the more homogeneous the micro structure will be. Notice that particles will have a more irregular shape and the particle size distribution will be wider. In addition, some surface contamination can occur by oxidation skin formation. Powder can be reduced by some kind of pre-consolidation treatment as annealing. sed for ceramic tool Powder compaction [pic] [pic] Rhodium metal: powder, pressed pellet (3*105 psi), remelted Powder compaction is the process of compacting metal powder in a die through the application of high pressures. Typically the tools are held in the vertical orientation with the punch tool forming the bottom of the cavity. The powder is then compacted into a shape and then ejected from the die cavity. [7] In a number of these applications the parts may require very little additional work for their intended use; making for very cost efficient manufacturing.

The density of the compacted powder is directly proportional to the amount of pressure applied. Typical pressures range from 80 psi to 1000 psi, pressures from 1000 psi to 1,000,000 psi have been obtained. Pressure of 10 tons/in? to 50 tons/in? are commonly used for metal powder compaction. To attain the same compression ratio across a component with more than one level or height, it is necessary to work with multiple lower punches. A cylindrical workpiece is made by single-level tooling. A more complex shape can be made by the common multiple-level tooling. Production rates of 15 to 30 parts per minutes are common.

A limited
time offer!
Get authentic custom
ESSAY SAMPLEwritten strictly according
to your requirements